（1）、biomass particles forming principle:
Biomass (mainly wood, sheet wood shavings) is the main component of cellulose, hemicellulose and lignin. When the biomass pellet heating heating temperature is between 200 ℃ -300 ℃ soft wood, at this time under the appropriate external force will depend on the adhesion of cellulosic biomass adjacent particles bond with each other.
（2）、Curing biomass stick with salary lubrication, plasticizer
Add a proportion: 2%
Ingredients: dry lubricants, plant cellulose, such as diluting carrier
Mechanism: When the plasticizer added to the raw materials were mixed after the molding machine under high temperature and pressure of water swelling and show the cohesion, while also part of the heat generated due to expansion so that uniform heating of biological particles (such uniform heat from the heating device and the pressure of the propeller is not, and it is the traditional processing density, low strength reasons), to gain high-density, high strength premium pay bar.
（3）、Two effects:
A、engine lubrication by reducing friction lubricant technology, part of the rods in the process of lubricant will be implemented in the sleeve and the screw propeller device to form a smooth contact surface friction layer
B、plasticizers with "enzyme - extraction" technique, extracts from plants, cellulose, and then dried - after two smashing pre-mixed, so that good dispersion of material rapidly coated biomass particles to increase the biomass degree of particle bonding glue.
（4）Lubricant, plasticizer use: (depending on raw materials may be)
A、 raw materials added after drying, this method was no loss, it is difficult to obtain suitable uniformity will ultimately affect the shape of raw materials. (High content of forming a good, occasionally poor pay intermittently stick)
B、 before drying increases of raw materials, raw materials pile up in the expected output when the dry ingredients by adding the number of (sub-level add), so that the transport process through the dryer will get the right mix uniformity.
C、 Add screening material, suitable for low temperature and raw material impurities. After the initial screening machine and dryer in the second hybrid hybrid will achieve the best uniformity, drawback is that a small amount of wear and tear.
（5）Suggested Use:
Low water content of dry material (such as wood shavings), added before the drying. For lubrication, plasticizers slightly larger than the proportion of the internal components of wood raw materials (and the food share similar) will not occur during drying loss; high water content of wet material (more than 30%) Add screening, if screening mix of completed 3-5 days of raw materials can be stacked, the remaining plasticizer enzyme in the appropriate temperature in the decomposition of the new material again, so that raw materials become easier to shape.