Flame Retardant Heavy Wall Heat Shrink Tubing With Adhesive
0 likes
China [CN] |
Property
|
Test Method
|
Typical Data
|
|
Operating temperature
|
IEC 216
|
-55 to 110℃
|
|
Tensile strength
|
ASTM D 2671
|
c
|
|
Tensile strength after aging
|
ASTM D 2671/158℃, 168hrs.
|
≥12MPa
|
|
Longitudinal shrinkage
|
UL224
|
0, -10%
|
|
Elongation at break
|
ASTM D 2671
|
≥400%
|
|
Elongation at break after aging
|
ASTM D 2671/150℃,168hrs.
|
≥300%
|
|
Dielectric strength
|
IEC 243
|
≥20KV/mm
|
|
Volume resistance
|
IEC 93
|
≥1014Ω.cm
|
|
Heat shock(225℃/4hrs)
|
ASTM D 2671
|
No cracking or flowing
|
|
Thermoplastic Adhesive
|
||
|
Water absorption
|
ISO 62
|
<0.2%
|
|
Softening point
|
ASTM D E28
|
85℃
|
|
Peel strength (PE)
|
DIN 30672
|
4 N/cm
|
|
Copper stability
|
ASTM D 2671
|
Non-corrosive
|
|
Resistance to fungus and decay
|
ISO 846
|
Pass
|
|
Normal
size
(mm)
|
As supplied (mm)
|
After recovered (mm)
|
*Style
|
Standard
length
(mm)
|
|
|
Inside diameter
(min.)
|
Inside diameter
(Max.)
|
Wall thickness
(mm)
|
|||
|
19/3.2
|
19
|
3.2
|
3.2
|
O
|
1000-1220
|
|
33/5.5
|
33
|
5.5
|
3.4
|
O
|
1000-1220
|
|
44.4/7.4
|
44.4
|
7.4
|
3.6
|
O
|
1000-1220
|
|
50.8/8.3
|
50.8
|
8.3
|
4.3
|
O
|
1000-1220
|
|
69.8/11.7
|
69.8
|
11.7
|
4.8
|
O
|
1000-1220
|
|
88.9/17.1
|
88.9
|
17.1
|
4.8
|
O
|
1000-1220
|
|
119.4/22.9
|
119.4
|
22.9
|
4.8
|
O
|
1000-1220
|
|
235/40
|
235
|
40
|
4.8
|
O
|
1000-1220
|
Click enlarge Image