Property
|
Test Method
|
Typical Data
|
Tensile strength
|
ASTM D 2671
|
14MPa
|
Elongation at break
|
ASTM D 2671
|
800%
|
Tensile strength after aging at 175°C for 168 hrs
|
ASTM D 2671
|
14MPa
|
Elongation after aging at 175°C for 168 hrs.
|
ASTM D 2671
|
350%
|
Flammability
|
UL 224 /VW-1
SAE-AMS-DTL-23053/5
|
Pass
|
Heat shock (250°C / 4 hrs.)
|
ASTM D 2671
|
No cracking
|
Cold bend test (-55°C / 4 hrs.)
|
ASTM D 2671
|
No cracking
|
Dielectric strength
|
ASTM D 150
|
22KV/mm
|
Volume resistance
|
ASTM D 876
|
1014Ω .cm
|
Copper Corrosion
|
UL 224
|
Pass
|
Water absorption
|
ASTM D 570
|
0.15%
|
Chemical resistance
|
SAE-AMS-DTL-23053/5
|
Pass
|
Longitudinal shrinkage
|
UL 224
|
0±5%
|
Eccentricity
|
UL 224
|
30%
|
Normal Size
(mm)
|
As supplied (mm)
|
After recovered (mm)
|
Standard
Length
(m/spool)
|
|
Inside
diameter
(mm)
|
Inside
diameter
(Max.)
|
Wall
thickness
(Min.)
|
||
3/64
|
1.2
|
0.6
|
0.33
|
200
|
1/16
|
1.6
|
0.8
|
0.36
|
200
|
3/32
|
2.4
|
1.2
|
0.44
|
200
|
1/8
|
3.2
|
1.6
|
0.44
|
200
|
3/16
|
4.8
|
2.4
|
0.56
|
100
|
1/4
|
6.4
|
3.2
|
0.56
|
100
|
5/16
|
8.0
|
4.0
|
0.56
|
100
|
3/8
|
9.5
|
4.8
|
0.56
|
100
|
1/2
|
12.7
|
6.4
|
0.65
|
50
|
5/8
|
16.0
|
8.0
|
0.69
|
50
|
3/4
|
19.1
|
9.5
|
0.80
|
50
|
1
|
25.4
|
12.7
|
0.90
|
50
|
11/4
|
31.8
|
15.9
|
0.90
|
50
|
11/2
|
38.1
|
19.1
|
1.02
|
50
|
2
|
50.8
|
25.4
|
1.02
|
50
|
3
|
76.2
|
38.1
|
1.20
|
30
|
4
|
101.6
|
50.8
|
1.30
|
30
|
Normal size(mm)
|
As supplied (mm)
|
After recovered (mm)
|
Standard length (m/spool)
|
|
|
|
|||||
|
|||||
Inside
|
Inside
|
Wall
|
|
||
diameter
|
diameter
|
thickness
|
|
||
(mm)
|
(Max.)
|
(Min.)
|
|
||
1.6/0.5
|
1.6
|
0.5
|
0.51
|
200
|
|
2.4/0.8
|
2.4
|
0.8
|
0.51
|
200
|
|
3.2/1
|
3.2
|
1.0
|
0.55
|
200
|
|
4.8/1.5
|
4.8
|
1.5
|
0.6
|
100
|
|
6.4/2
|
6.4
|
2.0
|
0.65
|
100
|
|
9.5/3
|
9.5
|
3.0
|
0.75
|
100
|
|
12.7/4
|
12.7
|
4.0
|
0.75
|
50
|
|
19.1/6
|
19.1
|
6.0
|
0.85
|
50
|
|
25.4/8
|
25.4
|
8.0
|
1.0
|
50
|
|
39/13
|
39.0
|
13.0
|
1.15
|
50
|