Military Grade, Fluid Resistant at High Temperature , Heat Shrink Identification Marker Sleeves

Quick Detail

Package & Delivery Lead Time

Detailed Description

MSVLO Military Grade, Fluid Resistant at High Temperature , Heat Shrink Identification Marker Sleeves  Description MSVLO series is military grade cable and wire identification sleeves, which is designed to meet the requirements of outstanding oil resistance. It is made of cross-linked environmentally friendly polyolefin bombarded by high power electron beam with electronic accelerators to meet high end markets where highly reliable cable& wire identification is required. MSVLO conforms to Classes 1 and 3 of AMS-DTL-23053/6, half-hard high molecular materials. Shrink ratios, both 2:1 and 3:1 are available. See below tables. MSVLO boasts amazingly high fluid resistance at high temperature for long time like JP-8 used for aviation fuel oil. It is widely used in aviation and spaceships, high speed rails EMU, submarine as well as other military and architecture industries.  Features  Fluid resistance at 70°C/158°F for 168h, such as JP-8 fuel oil, temperature rating 135°C /275°F  High temperature resistant, rated temperature, 135°C  Highly flame retardant, VW-1  ROHS compliant  High reliability, permanent identification  Heat sensitive, swift recovery  Computer-printable, any characters and logo are easy to design  Rated Temperature Continuous operating temperature: -55°C~135°C /-67°F~275°F Min. shrink temperature: 85°C /+185°F Full recovery temperature: 115°C~200°C /239°F~392°F, 8~3minutes Max. storage and transportation temperature: ≤50°C /122°F  Standards  Meets AMS-DTL-23053/5, compatibility: UL224  Color code soundness: SAE-AS 81531 and MIL-STD-202F/215J  Structure  Dimension(2:1, middle wall) Order Description Expanded As Supplied（mm） Recovered After Heating（mm） Inner Diameter ID1 Flatten width G Dual Wall Thickness H Inner DiameterID2 Single Wall Thickness h MSVLO-2X-1.6/ 2.00±0.20 3.7±0.3 0.48±0.10 ≤0.79 0.45±0.06 MSVLO-2X-2.4/ 2.79±0.20 5.0±0.3 0.48±0.10 ≤1.18 0.49±0.06 MSVLO-2X-3.2/ 3.64±0.23 6.3±0.4 0.48±0.10 ≤1.59 0.51±0.06 MSVLO-2X-4.8/ 5.26±0.25 8.9±0.4 0.49±0.10 ≤2.36 0.54±0.06 MSVLO-2X-6.4/ 6.92±0.28 11.5±0.4 0.50±0.10 ≤3.18 0.56±0.06 MSVLO-2X-9.5/ 10.2±0.32 16.7±0.5 0.51±0.11 ≤4.75 0.59±0.06 MSVLO-2X-12.7/ 13.5±0.36 21.8±0.6 0.52±0.11 ≤6.35 0.60±0.07 MSVLO-2X-19/ 20.1±0.40 32.2±0.6 0.53±0.11 ≤9.53 0.62±0.07 MSVLO-2X-25/ 26.7±0.45 42.5±0.7 0.55±0.12 ≤12.7 0.63±0.07 MSVLO-2X-38/ 39.8±0.51 63.2±0.8 0.57±0.12 ≤19.1 0.64±0.07 MSVLO-2X-51/ 53.0±0.56 83.9±0.9 0.58±0.13 ≤25.4 0.64±0.08 MSVLO-2X-76/ 79.4±0.56 125.3±1.0 0.59±0.13 ≤38.1 0.64±0.09  Dimension(3:1, middle wall) Order Description Expanded As Supplied（mm） Recovered After Heating（mm） Internal Diameter ID1 Flatten Width G Dual Wall Thickness H Inner Diameter ID2 Single Wall Thickness h MSVLO-3X-1.6/ 2.00±0.20 3.7±0.3 0.47±0.10 ≤0.53 0.52±0.06 MSVLO-3X-2.4/ 2.79±0.20 5.0±0.3 0.47±0.10 ≤0.79 0.57±0.06 MSVLO-3X-3.2/ 3.64±0.23 6.3±0.4 0.48±0.10 ≤1.06 0.61±0.06 MSVLO-3X-4.8/ 5.26±0.25 8.9±0.4 0.49±0.10 ≤1.59 0.67±0.06 MSVLO-3X-6.4/ 6.92±0.28 11.5±0.4 0.50±0.10 ≤2.36 0.71±0.06 MSVLO-3X-9.5/ 10.2±0.32 16.7±0.5 0.52±0.11 ≤3.18 0.77±0.06 MSVLO-3X-12.7/ 13.5±0.36 21.8±0.6 0.53±0.11 ≤4.75 0.80±0.07 MSVLO-3X-19/ 20.1±0.40 32.2±0.6 0.55±0.11 ≤6.35 0.84±0.07 MSVLO-3X-25/ 26.7±0.45 42.5±0.7 0.56±0.12 ≤8.47 0.86±0.07 MSVLO-3X-38/ 39.8±0.51 63.2±0.8 0.57±0.12 ≤12.9 0.89±0.07 MSVLO-3X-51/ 53.0±0.56 83.9±0.9 0.57±0.13 ≤17.2 0.90±0.08 MSVLO-3X-76/ 79.4±0.56 125.3±1.0 0.59±0.13 ≤25.8 0.92±0.09  Standard Packaging Data No. Sizes Packaging（Pcs/Reel） Box 210 Box 146 1 Φ1.6 2500 250 2 Φ2.4 2500 250 3 Φ3.2 2000 250 4 Φ4.8 2000 250 5 Φ6.4 1500 250 6 Φ9.5 1000 250 7 Φ12.7 500 250 8 Φ19 500 250 9 Φ25 500 250 10 Φ38 250 250 11 Φ51 250 250 12 Φ76 250 250  Physicochemical& Electrical Performance Properties Indicator Test Method Specific Property Unit States Tensile Strength Mpa Unaged ≥13.8 ASTM G 154,MIL-DTL-23053E ISO 37,500mm/min 175°C,168h,ISO 188 Heat aged/After fluid UV aged ≥11.1 Elongation at break % Unaged ≥200 Heat aged/After fluid ≥100 Secent Modulus Mpa Unaged ≥173 ASTM D 882 Voltage Withstand V Unaged/After aged 2500V,No breakdown in 60 sec. IEC 243,ASTM G 154 175°C,168h,ISO 188 Dielectric Strength MV/m Before ageing ≥19.7 Heat Aged/After fluidUV aged ≥15.8 Volume Resistivity Ω.cm Unaged ≥1014 IEC 93 Dielectric Constant - Unaged ≤3.2 ASTM 150 Water Absorption - Unaged ≤0.5 ASTM 570,23°C,24h Bare Copper Corrosion - Unaged No corrosion 23°C,Rh 95±5%,24h 175°C,16h Heat Shock - Unaged No cracks, flowing, dripping Wind to specified mandrel，225°C,4h Cold Flexibility - Unaged No cracks Wind to specified mandrel，-30°C,1h Flammability - Unaged VW-1 IEC 60332-1-3 Ed.1.0 b:2004 Longitudinal Change % Unaged 2X：-10~+1 200°C,constant temperature 3min 3X：-15~+5 Smoke Density - Unaged - DIN 5510-2 Toxicity Index - Unaged - BS 6853:1999 Appendix B Pls feel free to contact me if you have any questions! Contact: Jimmy Tel:+86-1377-6058-307 Skype: volsun-jimmy Facebook:www.facebook.com/jimmy.di.307

Basic Company Information

Suzhou Volsun Electronics Tech Co.,Ltd

Company Advantage

Detail Company Introduction