Product:AISI
Key words:shock resistance die steel,tool steel,die steel,Alloy Construction steel,alloy structure steel,flat steel,round steel,forged steel,hotwork steel,cold work steel,steel bar,flat bar,cold bar
Typical analysis:
C:0.50-0.60
Si:0.75-1.10
Mn:0.20-0.50
P:Max 0.030
S:Max 0.030
Cr:4.75-5.50
Mo:1.15-1.65
W:1.00-1.50
Advantages:
1.The most versatile cold work die steel. More toughness than A-2 or D-2. More wear resistance than S-7.
2.Very stable in heat treatment.
Availability:
Limited.
Applications:
A-8 combines good/wearing qualities with excellent toughness characteritics. It is well suited for many metal working dies and punches which operate in the hardness range of 55-60 Rockwell C.
Machinability:
A-8 has a machinability rating of 85% of a 1% carbon tool steel. It also has a high grindability rating.
Annealing:
Heat in an atmosphere furnace to 1550°F and hold for one hour per inch of thickness. Furnace cool at 25°F per hour maximum to 1000°F then air cool. The annealed hardness of A-8 is approximately 197 to 229 Brinell. Allow to heat slowly to the desired temperature and hold for a period of two hours. Remove from furnace and cool in still air. For most cold work applications tempering should be carried out in the range of 300° to 600°F. Doulbe tempering is recommended for best results with tempering temperatures above 600°F.
Other related Product grades:
1.2343,1.2344,1.2345,1.2436,1.080,1.2601,1.2550,1.2510,1.2714,1.12367,1.2365,1.2842,1.3343,1.3343,1.2083,1.2312,1.2316