RTV2 Moldmaking Platinum Cured Liquid Silicone Rubber LSR

Product

Posting date : Aug 29, 2022

Click enlarge Image

Membership

Free Member Scince Aug 29, 2022

FOB Price

$6.5

Min. Order Quantity

200KG

Supply Abillity

500ton/month

Port

SHENZHEN

Payment Terms

FOB

Package

Buckets & Drums

Keyword :

liquid silicone rubber

Product Description

Specification
Addition Cured Silicone Rubber for Mold Making, which is also named addition cure silicone rubber and platinum cure silicone rubber, is generally a two-component liquid silicone rubber vulcanized under room temperature(RTV-2).

Applications
Addition Cured Silicone Rubber has extensive use,such as mold making of foods (candy,cake, cookie,chocolate, ice cube, fondant etc), jewelries, tires, rapid prototyping,life casting,realistic mask,epoxy resin products,candle,vacuum foaming,making of prosthetic breast,artificial skin,human body,adult toys,baby feeding nipples,phone case and so on.

Techinical Parameters

Model Code	GTSIL-P10	GTSIL-P15	GTSIL-P20	GTSIL-P25	GTSIL-P30	GTSIL-P35	GTSIL-P40
Hardness - Shore A	8-10	14-16	19-21	24-26	28-30	34-36	38-42
Viscosity - Cps	3000-5000	4000-6000	4000-7000	5000-8000	6000-9000	6000-10000	4000-6000
Mixing Ratio - %	1:1	1:1	1:1	1:1	1:1	1:1	1:1
Tear Strength - KN/m2	14-17	16-18	18-22	22-26	20-23	16-19	12-16
Tensile Strength - Mpa	3.5-5.5	4-6	4-6	4-6	4-6	4-6	3.5-5.5
Shrinkage - %	0.10%	0.10%	0.10%	0.10%	0.10%	0.10%	0.10%
Elongation - %	500-600%	500-600%	500-600%	400-500%	400-500%	350-500%	300-450%

How to use

1.Substrate Preparation
The surface of the original should be clean and free of loose material. If necessary, and in particular with porous substrates, use a suitable release agent such as petroleum jelly or soap solution.

2. Mixing
Thoroughly stir Part A (silicone base) before use as filler separation may occur upon prolonged storage.
Weigh 100 grams Part A (silicone base) and 3 grams Part B (curing agent) in a clean container. Mix together until the curing agent is completely dispersed in the base. Hand or mechanical mixing can be used, but do not mix for an extended period of time or allow the temperature to exceed 35°C (95°F). Mix suitably small quantities to ensure thorough mixing of the par A (silicone base) and part B (curing agent).

It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 minutes under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture, so a suitably large container should be chosen.

Caution: prolonged vacuum will remove volatile components from the mix and may result in poor thick section cure and non-typical properties.

Note: If no vacuum de-airing equipment is available, air entrapment can be minimized by mixing a small quantity of par A (silicone base) and part B (curing agent), then using a brush, painting the original with a 1-2mm layer. Leave at room temperature until the surface is bubble free and the layer has begun to cure. Mix a further quantity of base and curing agent and proceed as follows to produce a final mold.

3. Pouring the Mixture and Curing
Pour the mixed Par A (silicone base) and Part B (curing agent) as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 24 hours at room temperature (22°C-24°C/ 71.6°F - 75.2°F) and the mold can then be separated from the original. If the working temperature is significantly lower, the cure time will be longer. If the room temperature or humidity is very high, the working time of the catalyzed mixture will be reduced. The final mechanical properties of the mold will be reached within 7 days.