Low friction Dacromet Coating friction coefficient of small 0.12-0.18 PH 3.8-5.2 Product Description
JH-9510 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.
Performance characteristics:
The film is silver white, good surface finish, high corrosion resistance, and then good friction coefficient of small 0.12-0.18
Coating Process:
1. Mix Ratio
Pack A: Pack B: Pack C=1:1: X(according to different viscosity demand )
2. Before Mixture, Keep weighted A&B into the water bath at 252 , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.
3. Add B to the stirring A slowly.
4. Stir the mixture about 1~2 hours after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30, otherwise C will not be dissolved sufficiently .)Then stir 12 hours alowly and continuously.
5. The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.
6. Temperature control device should be equipped with dip barrel to keep the temperature of coating at 222.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.
7. Test Specific gravity,PH,Temperature,Viscosity of coating every 8 hours if operate continuously.
Technical data:
- - - -
No. | Item | Data |
1 | Color | Silver |
2 | Coating method | Dip Spin & Spraying |
3 | PH | 3.8-5.2 |
4 | Specific gravity | 1.330.05 (spray coating) 1.330.05(dip-spin coating) |
5 | Viscosity | 20~60seconds(spray coating) 60-80seconds(dip-spin coating) |
6 | Operating temperature | 202 |
- - - -
Mix Diagram:
Coating Process:
Attentions:
Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.
Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .
It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.
The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.