Name
|
chemical composition(%)
|
|||||||
C
|
Si
|
Mn
|
Cr
|
Mo
|
Cu
|
P
|
S
|
|
Ordinary high chromium ball
|
2.0-3.3
|
≤1.2
|
0.3-1.5
|
10-13
|
0-3.0
|
≤1.2
|
≤0.1
|
≤0.06
|
Special high chromium ball
|
2.0-3.3
|
≤1.2
|
0.3-1.5
|
15-23
|
0-3.0
|
≤1.2
|
≤0.1
|
≤0.06
|
Name
|
Surface hardness
(HRC)
|
Impact value(J/cm2)
|
Metallographic structure
|
Falling ball impact fatigue service life
|
|
Ordinary high chromium ball
|
≥58
|
≥4
|
M+C+A
|
≤Φ80
|
≥15000
|
≥Φ80
|
≥10000
|
||||
M- martensite C- carbide A- retained austenite
|
specification(mm)
|
unit weight
(kg)
|
quantity(pc/t)
|
|
specification(mm)
|
Unit weight(kg)
|
quantity(pc/t)
|
Φ30
|
0.11
|
9091
|
Φ90
|
2.90
|
345
|
|
Φ40
|
0.25
|
3891
|
Φ100
|
4.00
|
250
|
|
Φ50
|
0.50
|
2000
|
Φ110
|
5.30
|
188
|
|
Φ60
|
0.86
|
1153
|
Φ120
|
6.80
|
147
|
|
Φ70
|
1.37
|
729
|
Φ130
|
7.70
|
129
|
|
Φ80
|
2.05
|
487
|
Φ140
|
8.74
|
114
|