ASTM A333 Grade 8 Seamless Pipes
0 likes
China [CN] 
ASTM A333 Standard covers seamless and welded steel pipe for low temperature service. The Grade 8 steel involved is similar to AISI 4032 low alloy steel. ASTM A333 Grade 8 pipe shall be made by the seamless or welding process with the addition of no filler metal in the welding operation.
Seamless and Welded Steel Pipe size for Low-Temperature Service:
Application: Seamless and Welded Steel Pipe for Low-Temperature Service.Steel grade: ASTM A333 Grade 8
Inspection and Test:
| Crade | The lowest temperature for strike test | |
| ℉ | ℃ | |
| ASTM A333 Grade 8 | -320 | -195 |
ASTM A333 Gr. 8 Chemical Compositions(%)
| Grade | Chemical Composition (%) | ||||||
| C(max) | Si | Mn | P(max) | S(max) | Cr | Ni | |
| Grade 8 | 0.13 | 0.13-0.32 | 0.9 | 0.025 | 0.025 | -- | 8.40-9.60 |
ASTM A333 Gr.7 Mechanical Properties
| Grade | Tensile Strength (MPa） | Yield Point (MPa) | Elongation (%) | |
| Y | X | |||
| ASTM A333 Grade 8 | ≥690 | ≥515 | ≥22 | -- |
Impact temperature
Minimum Impact Test Temperature -45 C(-50 F)
| Size | Minimum Average Notched Bar Impact Value of Each Set of Three Specimens | Minimum Notched Bar Impact Value of One Specimen Only of a Set | ||
| Size of Specimen, mm |
ft-lbf
|
J
|
ft-lbf
|
J
|
| 10 by 10 |
13
|
18
|
10
|
14
|
| 10 by 7.5 |
10
|
14
|
8
|
11
|
| 10 by 6.67 |
9
|
12
|
7
|
9
|
| 10 by 5 |
7
|
9
|
5
|
7
|
| 10 by 3.33 |
5
|
7
|
3
|
4
|
| 10 by 2.5 |
4
|
5
|
3
|
4
|
Straight line interpolation for intermediate values is permitted.
| Specimen Width Along Notch or Actual Material Thickness mm | Temperature Reduction,Degrees Colder C |
| 10 (standard size) | 0 |
| 9 | 0 |
| 8 | 0 |
| 7.5 (3/4 standard size) | 3 |
| 7 | 4 |
| 6.67 (2/3 standard size) | 5 |
| 6 | 8 |
| 5 (1/2 standard size) | 11 |
| 4 | 17 |
| 3.33 (1/3 standard size) | 19 |
| 3 | 22 |
| 2.5 (1/4 standard size) | 28 |
|
ASTM A333
|
Grade 6
|
| P Number |
1
|
| Group |
1
|
Machinability
Machinability is good, similar to law alloy 4032 steel.
Forming
The product comes in piping form but may be formed readily by conventional methods.
Welding
Weldable by conventional methods.
Heat Treatment
Product is supplied in the normalized, 1500 f and air cooled, condition. It may be quenched and tempered by heating to 1475 F, quench in circulating water and then temper by re-heating to 1100 F and rapid air cooling.
Forging
Product is supplied in pipe form and not normally forged from that shape.
Hot Working
Hot working may be done qt 2000 F down to 1600 F if need be. Do not hot work below 1550 F and immediately following hot working cool in a controlled atmosphere furnace from a temperature above 1550 F.
Cold Working
Cold working may be done by conventional methods.
Annealing
Anneal, or normalize, at 1600 F and air cool.
Strike Temperature Condition
| Grade | The lowest temperature for strike test | |
| ℉ | ℃ | |
| ASTM A333 Gr.6 | -150 | -100 |
Packing:
Delivery:
Pipes are supplied in hexagonal bundles or round bundles tied with steel strip.Weight of bundle – up to 5000 kg upon request of customer.Each bundle is furnished with three tags.