RTV-2 Silicone for Architectural Decoration Moldmaking

Description of RTV-2 Silicone for Architectural Decoration Moldmaking:RTV-2 silicone rubber is a two component elastomeric cross-linking at room temperature. The polymerization can be accelerated by heat (max. 1500 C). The silicone components are delivered as liquids, which once mixed and cured transform into a translucent, elastic and resistant material. Polymerization occurs without formation of heat.Features of RTV-2 Silicone for Architectural Decoration Moldmaking:1. Good flow ability and long working time2. Medium hardness3. High tear and tensile strength4. Easy de-mould from complex replica parts5. Acid and alkali-resistance6. Low linear shrinkageApplications of RTV-2 Silicone for Architectural Decoration Moldmaking:RTV-2 Silicone are suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc.How to make the silicone mold?1. PreparingThe surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.2. MixingPlease weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35° C (95° F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.3. Pouring the mixture and curingPour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.Storage of RTV-2 Silicone for Architectural Decoration Moldmaking:When the silicone rubber is stored at or below 30 centi degree in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 10 months from the date of production. After 10 months stockpiles use the Stir to mix the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.Package of RTV-2 Silicone for Architectural Decoration Moldmaking:Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drumPart B CA30 Curing Agent: 800g/bottle, 1kg/bottleShould you have any question, please feel free to contact Ms Michelle.MINGCHENG GROUP LIMITED

Item No.:	MCSIL-H25
Color:	White
Viscosity:	35000 cps
Hardness:	28 shore A
Mix Ratio:	100:2
Pot life:	30-40 minutes
Curing time:	4-6 hours
Tensile strength:	4.5 Mpa
Tear Strength:	32 N/mm
Elongation:	511%
Shrinkage:	0.2-0.4%

TEL : 0086-769-82693920 / FAX : --
No.3, Chuang Ye 2nd Rd., He Lu Industrial Zone, Huang Jiang Guang Dong Dong Guan China [CN]
Homepage : http://www.mcsilicone.com

Main Products