Virgin ,recycled ,transparent LDPE resin | LDPE granules |LLDPE raw material price
0 likes
Thailand [TH] Best price!! Supply LDPE-Low density polyethylene
Introduce:
LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc...They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams.
Properties:
LDPE has good toughness, low temperature resistance, creep, and large thermal expansion.
LDPE is easy to process molding, can be extrusion, blow molding.
Specification:
LDPE Injection Grade
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
15 |
g/10min |
|
Density |
0.922 |
g/cm3 |
|
Tensile Yield Strength |
7 |
Mpa |
|
Elongation at Break |
75 |
% |
|
Wien Softening Point |
85 |
C |
|
Packing |
In 25 kg PP woven bags,18MT/20’FCL |
|
LDPE Blown Grade
|
Item |
Test Condition |
Test Method |
Value |
Unit |
|
Density |
|
ISO 1183 |
0.950 0.955 |
g/cm |
|
MFR |
190°C/2.16kg |
ISO 1133 |
1.7 2.5 |
g/10min |
|
Tensile strength at yield |
|
ISO 527-2 |
24 |
MPa |
|
Elongation at break |
|
ISO 527-2 |
600 |
% |
LDPE film grade
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
2 |
g/10min |
|
Density |
0.9225 |
g/cm3 |
|
Tensile Strength |
9 |
Mpa |
|
Elongation at Break |
500 |
% |
|
Fish eye max(0.3-2mm) |
30 |
n/1200cm2 |
|
Stripes |
20 |
cm/20m3 |
|
Packing |
In 25 kg PP woven bags,18MT/20’FCL |
|
Click enlarge Image