XK-P50-P
|
XK-P80-P
|
unit
|
Test Method
|
||
Thickness
|
1.0/1.5
|
1.0/1.5
|
mm
|
||
Color
|
Dard Red
|
gray
|
|
Visual
|
|
Construction
|
Silicone
|
|
|
||
Op. temp. range
|
-45~150
|
-45~150
|
℃
|
|
|
Density
|
3.1
|
3.3
|
g/cm3
|
ASTM D792
|
|
Thermal Conductivity
|
6
|
8
|
W/mK
|
ASTM D5470
|
|
Breakdown Voltage
|
13
|
11
|
KV/mm
|
ASTM D149
|
|
Volume Resistance
|
1010
|
1010
|
Ohm-cm
|
ASTM D257
|
|
Total Mass Loss
|
<0.4%
|
<0.4%
|
%
|
ASTM E595
|
|
Tensile strength
|
na
|
na
|
psi
|
ASTM D412
|
|
Elongation
|
na
|
na
|
%
|
ASTM D412
|
|
Flame Rating
|
V-0
|
V-0
|
|
UL-94
|
|
REACH/RoHS Compliant
|
Yes
|
Yes
|
REACH/ RoHS
|
|
XK-P50-P
|
XK-P80-P
|
RA
|
( Kin2/W)
|
( Kin2/W)
|
compress30%
|
0.24
|
0.18
|
compress40%
|
0.22
|
0.15
|
compress50%
|
0.20
|
0.12
|
compress70%
|
0.15
|
0.11
|
compress90%
|
0.12
|
0.08
|
|
XK-P50-P
|
XK-P80-P
|
Pressure(psi)
|
Pressure (psi)
|
|
Compress30%
|
11
|
12
|
Compress40%
|
27
|
29
|
Compress50%
|
46
|
49
|
Compress70%
|
56
|
61
|
Compress90%
|
77
|
85
|