isostatic graphite crucible for jewerly
0 likes
China [CN] The crucible is an utensil or melting tank vessels that is made of refractory material (such as clay, graphite, quartz or difficult molten metal iron, etc.).
Graphite crucible, with is special advantages and Plasticity, is widely used in the smelting area, e.g. gold smelting, silver smelting, aluminum smelting, cooper smelting, etc.
Material Specifications:
| Item | Unit | Isostatic graphite |
| grain size | μm | 5-22 |
| Bulk density | g/cm3 | 1.8-1.85 |
| Specific resistance | μΩ.m | <=15 |
| Bending strength | MPa | >=40 |
| Compressive strength | MPa | >=85 |
| Shore hardness | >=65 | |
| C.T.E.(100-600) °C | 10-6/°C | 4.0-5.2 |
| Modulus of elasticity | GPa | 10-12.5 |
| Ash | % | <=0.03% |
| Fine-grain Specialty Graphite FXG-1 | Fine-grain Specialty Graphite FXG-2 | ||||
| Item | Unit | Guarantee value | Typical value | Guarantee value | Typical value |
| Max grain size | mm | 0.8 | 0.8 | 0.8 | 0.8 |
| Bulk density | g/cm3 | ≥1.70 | 1.73 | ≥1.73 | 1.76 |
| Specific resistance | μΩ.m | ≤8.5 | 7.5 | ≤8.0 | 7 |
| Bending strength | MPa | ≥10.0 | 11 | ≥12.0 | 12.5 |
| Compressive strength | MPa | ≥24.0 | 27 | ≥31.0 | 34 |
| Thermal Condcutivity | W/(m.k) | ≥120 | 150 | ≥130 | 160 |
| C.T.E.(100-600) °C | 10-6/°C | ≤2.5 | 2.2 | ≤2.5 | 2.1 |
| Ash content | % | ≤0.3 | 0.09 | ≤0.3 | 0.09 |
| high pure graphite | ||||
| Item | Unit | baked twice | baked three time | baked four times |
| impregnated once | impregnated twice | impregnated three times | ||
| grain size | mm | ≤325mesh | ≤325mesh | ≤325mesh |
| Bulk density | g/cm3 | ≥1.68 | ≥1.78 | ≥1.85 |
| Specific resistance | μΩ.m | ≤14 | ≤14 | ≤13 |
| Bending strength | MPa | ≥25 | ≥40 | ≥45 |
| Compressive strength | MPa | ≥50 | ≥60 | ≥65 |
| Ash content | % | ≤0.15 | ≤0.1 | ≤0.05 |
Using Field:
1. often used in metallurgy, casting, mechanical, chemical and other industrial sectors
2. Widely used in smelting the alloy tool steels, nonferrous (e.g. gold,silver,aluminum, etc), nonferrous metal alloy, jewelry, glass and other suitable area.
Advantages of the crucibles:
1.good thermal conductivity
2.High-temperature resistance
3.Small thermal expansion coefficient.
4.Strong corrosion resistance to acid and alkali liquid
5.Good chemical stability
Operating Notice:
1.The crucible should be stocked in the dry situation
2.Carry the crucible lightly
3.Warm the crucible in the drying machine or near the furnace.The warming temperature should be up to 500℃.
4.The crucible should be put under the furnace month flat.
5.When put the metal into the crucible, you should take the crucible capacity as your reference.If the crucible is too full,it will be damaged by expansion.
6.The clamps shape need as that of crucible.Avoid the concentrate stressed destroy of the crucible
7.Clean the crucible regularly and lightly.
8.The crucible should be put in the center of the furnace and leave some distance between the crucible and furnace.
9.Turn the crucible once in one week and this will help lengthen the service life.
10.The flame should not touch the crucible directly.