Model
|
standard length
|
width(mm)
|
Net Weight(kg)
|
RF003-0.30MM
|
260
|
950
|
110
|
RF005-0.50MM
|
175
|
950
|
110
|
RF007-0.70MM
|
125
|
950
|
110
|
Performance
|
Test Methods
|
unit
|
Magnitude
|
Melting index
|
ISO 1133
|
cm3/10min
|
8
|
Reflectivity
|
|
|
96~98%
|
Density
|
ISO1183
|
Kg/m3
|
1200
|
Water Absorption
|
ISO62
|
%
|
0.2
|
Tensile modulus
|
ISO 527-1
|
MPa
|
2400
|
Tensil strength at yield
|
And
|
MPa
|
61
|
Tensile strength elongation
|
ISO 527-2
|
%
|
6
|
Norminal elongation at tensile fracture
|
|
%
|
>50
|
Bending Modulus
|
ISO 178
|
MAa
|
2350
|
Bending Strength
|
ISO 178
|
MAa
|
93
|
Izod notched impacted strength
|
ISO 179
|
KJ/㎡
|
76
|
Heat deflection temperature
|
ISO 75-1
|
℃
|
129
|
Vicard softening temperture
|
ISO 306
|
℃
|
149
|
Molding shrinkage
|
Customized method
|
%
|
0.5~0.7
|
Coefficient of linear expansion
|
ISO 11359-2
|
×10-4 /℃
|
0.7
|
Dielectric constant
|
IEC 60250
|
-
|
3.1
|
|
|
|
3
|
Dielectric loss tangent
|
IEC 60250
|
×10-4
|
10
|
|
|
×10-4
|
90
|
Volume Resistivity
|
IEC 60093
|
Ω.m
|
>1×1013
|
Surface Resistivity
|
IEC 60093
|
Ω
|
>1×1015
|
Voltage withstand
|
IEC 60243-1
|
MV/m
|
30
|
ARC Resistance
|
IEC 60112
|
-
|
250
|
Flame Retardance
|
UL 94
|
-
|
V-2(0.4mm)
|
|
|
|
HB(1.5mm)
|