stainless steel plate grades standard steel plate size

custom metal plates , custom metal tags.  Name Plate Manufacturers,Custom Name plates,Metal Tags,Metal Labels,Signs, Decals in China. 

 

China Name Plate Manufacturers,we custom name plates, brass plate engraving.  metalphotos,tags,labels,signs,decals with logo and printing. 

 

Material:Metal,Aluminum,Anodized Aluminum,Brass,Stainless Steel,Polycarbonate,Polyester,Vinyl. 

 

Website: www.nameplatesmanufacturers.com   metal plate manufacturers

 

characteristics. Used in machinery, electronics, instruments, meters, household appliances, hardware, watches, cosmetics and packaging. Pre-treatment of aluminum substrates have a variety of methods, depending on the use, mainly degreasing, sandblasting, wire drawing, polishing, oxygen grease.1, oil: the surface of an aluminum substrate with a certain affinity Hu ink, the need to remove surface oil and oil, can wipe cotton dipped in gasoline. It can also be used for chemical degreasing alkaline solution, such as sodium sulphate 30-50 g / l, sodium 40-60 g / l, sodium 10-15 g / l, at a temperature of 60-70 degrees immersed 2-5 minutes degreasing.2, sandblasting: sandblasting to improve the adhesion of the ink and the metal material is generally used sandblasting machine dedicated for discharging treatment, if 0.5-1 mm thick aluminum plate, sandblasting sand of 0.05 to 0.15 mm in diameter, and available river sand, sieve after use.3, drawing: also known as twist processing is the processing method of the delicate mechanical friction straight lines in the aluminum surface. It was a relatively new decorative surface treatment process, we can overcome the defects such as scratches on the aluminum surface. Improve utilization of materials. There are two thick wire drawing lines to find ways and filaments, usually with a diameter of 0.1 mm stainless steel wire brush or scouring pad brush, nylon belt can also be processed.4, polishing: to overcome the aluminum material surface defects and improve surface finish. Polishing and chemical mechanical polishing polishing points. It is the use of mechanical polishing cloth polishing wheel machine, multi-chemical polishing is carried out in an acidic solution, such as 15% sulfuric acid, 10% nitric acid, the temperature of 90-100 degrees, time of 2-3 minutes.5, oxide: aluminum surface polished has a residual soap polishing, wipe application boards yarn dipped in gasoline and chemical degreasing, then immersed in a nitric acid solution (1 to 1 ratio of nitric acid and water), removed after 10 minutes, and then into the oxidation tank electrochemical oxidation. Oxidizing liquid formula: nitrate 160-200 g / ml, temperature of 10-20 degrees, 30 minutes. Good sufficiently washed with water dried aluminum oxide, formed on the surface layer of uniform porosity in the oxide layer, i.e., oxide film, to avoid dirt contamination. Good aluminum oxide immediately print the best, if not immediately printed, soft paper application septum wrapped or dried directly on the shelves, storage time should not exceed one week. The surface of the aluminum oxide layer can absorb dye, water and other salts, it is not something with greasy hands or contact surface when printing. When the ink is printed onto the oxide layer, namely the ink penetrate pores. Heating the next step is to accelerate the ink to penetrate pores until all the pores in the surface of the ink-covered been filled so far. Few printed ink surface diffusion or non-proliferation, to ensure good text, graphics precision and clarity.6, closed: its role is firmly sealed in the ink within the pores, and never rise overflow or diffusion. No ink coverage to complement the site is closed to fill the role of the oxide film is also the gap, making it impervious to enhance corrosion resistance surface. Generally use nickel sulfate solution for blocking. Recipe: Chinese NICKEL 10-12 ml, temperature 80-90 degrees, 10-15 minutes. Hand or other things and then sealing with oil contact surface with the general cleaning agents can be washed off.Silk screen printing ink (paint)