Apollo seiko DCS-08PC Nitregen Soldering tip cartridge DCS series tips Apollo tips

China [CN]

Apollo solder tips DCN series:

Leisto's production Apollo Seiko compatible soldering tips have good performance such as low temperature difference (plus-minus 10 degree),smooth solder wetting performance.The great base copper & precise plating technology improves the thermal conductivity and reduce the temperature recovery time.The soldering tip can make the robots get the most out of automated soldering:working stable,low faulty soldering joints.

Specifications of Apollo DCN-08D Soldering Tip:

• Two side tinning
• DC48V, Total Length: 101mm
• Diameter: 6.4mm
• Tip width: a: 3mm, b: 0.8mm
• Tip thickness (c): 0.3mm
• Tin area, two side (d): 0.8mm

Advantages of Leisto Soldering Tip:

1. -Made with pure oxygen-free copper
2. - Long time electroplating makes the plating layer more denser, the life time is longer than other tips
3. - Short lead time for standard robot tips
4. - The cost is much lower than original tips
5. - Custom made available

Tip Cleaning Notes:

1. If the sponge cleaner is utilized, air-blow cleaning is normally not required.
2. Some applications require air-blow & sponge tip cleaning (depending upon tip type)
3. Standard cleaning duration is 0.5 second
4. The iron tip does not need to be extended if not required
5. The air-blow cup is not included with the standard Luna system

If the tip is not wetting with solder (oxidation): 

• Remove pre-solder on tip completely.
• Remove oxidation by sand paper after cooling down the iron tip to room temperature.
• Turn on the power and apply solder on the iron tip during rising the temperature (manually).

The tip will wet with solder by the above process.