we have more than 40 years experience in this industry
specially for cement machinery,such as gear ring
Material:Carbon steel,low alloy steel:ZG20SiMn,ZG50Mn,ZG35SiMn,ZG35CrMo,ZG35SiMnMo,
ZG42CrMo,ZG40Cr,ZG34CrNiMo,ZG40Mn ZG35CrNiMo6, ZG35CrMo4 and so on.
Process:Place a pattern in sand to create a mold; Incorporate a gating system; Remove the pattern;Fill the mold cavity with molten metal;Allow the metal to cool;Break away the sand mold and remove the casting.
Standard&certificate:ASTM,BS,NF,DIN,JIS and so on; ISO 9001:2000
Weight:from 3 tons to 120 tons per piece
Application:
The products can be widely used in the area of cement mill,rotary kiln,shipbuilding,
metallurgy,mine,sugar mill,powder plant,rail road,engine bed and so on.
We can provide OEM service for cement mill and rotary kiln casting parts,marine steel casting parts,sugar mill machinery parts with carbon steel or low alloy steel.
The casting parts can be supplied as following treatment:
Heat Treatment: Normalized, normalized and tempered,quench and tempered
Machining: Rough machined,semi-finished machined,finished machined
Quality warranty and testing equipment:
Magnetic powder inspection
UT nondestructive test
Dye inspection
Leeb hardness testing equipment
Machinery performance testing equipment
Metallographic microscope
Direct-reading spectrometer
Features of our products:
Durable
Excellent tensile strength
Accurate level of tolerance
Resistance to corrosion
Resistance to extreme temperature conditions
Good dimensional accuracy
Superb surface finishing
Easy to use and install
Possible defects:
Defect
Causes
Unfilled sections
Insufficient material
Low pouring temperature
Porosity
Melt temperature is too high
Non-uniform cooling rate
Sand has low permeability
Hot tearing
Non-uniform cooling rate
Surface projections
Erosion of sand mold interior
A crack in the sand mold
Mold halves shift
There are no these problems for us.
Uniform wall thickness will ensure uniform cooling and reduce defects. A thick section, often referred to as a hot spot, causes uneven cooling and can result in shrinkage, porosity, or cracking.
Corners
Round corners to reduce stress concentrations and fracture
Inner radius should be at least the thickness of the walls
Machining allowance
Add 0.0625 - 0.25 in. (0.16 - 0.64 mm) to part dimensions to allow for machining to obtain a smooth surface.