The Grade of the Tungsten Carbide Rods
|
|||||
Properties of Grade
|
RD10F
|
RD10UF
|
RD12UF
|
RD06UF
|
|
Co
|
%
|
10
|
10
|
12
|
6
|
WC incl. Doping
|
%
|
90
|
90
|
88
|
94
|
Density
|
g/cm3
|
14.45
|
14.45
|
14.1
|
14.9
|
Vickers Hardness HV30
|
kg/mm2
|
1580
|
1790
|
1690
|
1890
|
Rockwell Hardness HRA
|
ISO3738
|
91.8
|
93
|
>92.5
|
93.5
|
TRS
|
N/mm2
|
3800
|
4000
|
4000
|
3900
|
Porosity
|
A
|
< 02
|
< 02
|
< 02
|
< 02
|
B
|
0
|
0
|
0
|
0
|
|
C
|
0
|
0
|
0
|
0
|
|
WC Grain Size
|
μm
|
0.8
|
0.5
|
0.4-0.5
|
0.5
|
Part No.
|
Dia.mm
|
(Tol.)mm
|
I.d(d,mm)
|
tolerance(mm)
|
Lengthmm
|
Tolerancemm
|
1-2.0-330-s
|
2.0
|
+0.5/+0.3
|
0.5
|
±0.08
|
330
|
+3/0
|
1-3.0-330-S
|
3.0
|
+0.5/+0.3
|
0.50
|
±0.08
|
330
|
+3/0
|
1-4.0-330-S
|
4.0
|
+0.5/+0.3
|
0.80
|
±0.08
|
330
|
+3/0
|
1-5.0-330-S
|
5.0
|
+0.5/+0.3
|
0.80
|
±0.08
|
330
|
+3/0
|
1-6.0-330-S
|
6.0
|
+0.5/+0.3
|
1.00
|
±0.1
|
330
|
+3/0
|
1-7.0-330-S
|
7.0
|
+0.5/+0.3
|
1.00
|
±0.15
|
330
|
+3/0
|
1-8.0-330-S
|
8.0
|
+0.5/+0.3
|
1.00
|
±0.15
|
330
|
+3/0
|
1-9.0-330-S
|
9.0
|
+0.5/+0.3
|
1.40
|
±0.15
|
330
|
+3/0
|
1-10.0-330-S
|
10.0
|
+0.5/+0.3
|
1.40
|
±0.15
|
330
|
+3/0
|
1-11.0-330-S
|
11.0
|
+0.5/+0.3
|
1.40
|
±0.15
|
330
|
+3/0
|
1-12.0-330-S
|
12.0
|
+0.5/+0.3
|
1.50
|
±0.15
|
330
|
+3/0
|
1-13.0-330-S
|
13.0
|
+0.5/+0.3
|
1.75
|
±0.15
|
330
|
+3/0
|
1-14.0-330-S
|
14.0
|
+0.5/+0.3
|
1.75
|
±0.15
|
330
|
+3/0
|
1-15.0-330-S
|
15.0
|
+0.5/+0.3
|
2.00
|
±0.20
|
330
|
+3/0
|
1-16.0-330-S
|
16.0
|
+0.5/+0.3
|
2.00
|
±0.20
|
330
|
+3/0
|
1-17.0-330-S
|
17.0
|
+0.5/+0.3
|
2.00
|
±0.20
|
330
|
+3/0
|
1-18.0-330-S
|
18.0
|
+0.5/+0.3
|
2.00
|
±0.25
|
330
|
+3/0
|
1-19.0-330-S
|
19.0
|
+0.5/+0.3
|
2.00
|
±0.25
|
330
|
+3/0
|
1-20.0-330-S
|
20.0
|
+0.5/+0.3
|
2.50
|
±0.25
|
330
|
+3/0
|
1-21.0-330-S
|
21.0
|
+0.5/+0.3
|
2.50
|
±0.25
|
330
|
+3/0
|
1-22.0-330-S
|
22.0
|
+0.5/+0.3
|
2.50
|
±0.25
|
330
|
+3/0
|
1-23.0-330-S
|
23.0
|
+0.5/+0.3
|
2.5
|
±0.25
|
330
|
+3/0
|
1-24.0-330-S
|
24.0
|
+0.6/+0.4
|
3.00
|
±0.25
|
330
|
+3/0
|
1-25.0-330-S
|
25.0
|
+0.6/+0.4
|
3.00
|
±0.25
|
330
|
+3/0
|
1-25.4-330-S
|
25.4
|
+0.6/+0.4
|
3.0
|
±0.25
|
330
|
+3/0
|