1.Description of liquid silicone rubber
C830 Silicone rubber is condensation cure silicone rubber for mold making. The silicone rubber will be cured under room temperature, It’s two-components, the mixing ratio is 100:2 . Part A is a flowable liquid silicone , part B is the catalyst. It has an exceptional fluidity and good operability. C-830 tin cure mold silicone has a good property , it is suitable for various mold making .
2.Characteristics of liquid silicone rubber
*An exceptional fluidity and good operability, easy to demold*Good tensile strength and tear strength*lower shrinkage *non-deformation ,non-oily *good flexibility
*eco-friendly
*long shelf-time &lifetime
3.Application of liquid silicone rubber
stone mold ,concrete mold , cement casting mold
polyurethane casting mold , GRC casting mold , fiberglass cating mold
statue mold , sculpture mold , resin craft mold ,artificial wooden mold
gypsum mold , plaster mold ,bronze casting mold
candle mold ,soap mold, shoe mold , tyre mold ,etc .....
C830 Silicone rubber is mainly suitable middle sized product and big size with simple pattern.
4.Datesheet of liquid silicone rubber
|
Item No.
|
Appearance
|
Hardness (shore A°)
|
Viscosity (CPS)
|
Tensile-strength( kgf /cm2 )
|
Tear-strength (kgf /cm2 )
|
Elongation-break(%)
|
Mixing ratio
|
operation time (25 ℃)
|
Curing time( 25℃)
|
shrinkage
|
|
C830
|
White
|
30±2
|
22000±1000
|
≥45
|
≥26
|
≥480
|
100:3
|
20-30 mins
|
2~3 h
|
≤0.3%
|
5. Using instructions of liquid silicone rubber
Step 1: prepare and clean the prototype.You must make sure your original molds perfect. fix the original mold on a board , then using some assistant material(like cardpaper) to make a frame for to surround the prototype. The frame is no need ,if we make the mold by brushing way .
Step 2: Take the silicone and catalyst as the ratio 100:2 (silicone:catalyst=100:2) ,mix the silicone rubber and catalyst evenly. *Notes: Molding silicon rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of flowing liquid and part B is the curing agent. Remember to mix part A and part B evenly, otherwise the silicon rubber will be partly solidified and this will bring troubles for your final operation. What’s more, the finished molds will have a short life. All of these will cause a waste of silicon rubber.
Step 3: Vacuum pumping
After mixed the silicone evenly, it is better to release the bubble by Vacuum pumping.
Step 4: Pouring cast or brushing cast
After released the bubble, we can pour/brush the silicone rubber on the prototype *Notes:Please finished all the steped within the operation time .If not it will cause cross linking reaction, and no more further steps will be available.So,we have to pay attention to the pot life and curing time.
Package:
1kg/drum,5kgs/drum,20kgs/drum,25kgs/drum,200kgs/drum based on vacuum packing.
Shelf life and transportation
1. Twelve(12) months when stored at 25C in tightly closed original packages.
2. This kind of product is non-dangerous product, which could be transported as general chemicals.
Why you choose us ??
1.Free Sample
2.Sample Test
3.Technical Support
4.Engineers Site Instruction
5.New products developing
6.New Market developing
7.Factory Visiting Reception
8.China visiting reception
9.China Latest silicone news
10.Related Products Purchasing Assistance
11.More than 8 years experience in producing liquid silicone rubber
Any inquiry, feel free to contact Ms. Rachel: