Item No.
|
Appearance
|
Hardness
(shore A)
|
Viscosity (CPS)
|
Tensile-strength( kgf /cm2 )
|
Tear-strength
(kgf /cm2 )
|
Elongation-break(%)
|
Mixing ratio
|
operation time
(25 ℃ )
|
Curing time( 25 ℃)
|
Shrinkage
(%)
|
SP-805
|
translucent
|
5
|
3000±1000
|
30±5
|
8±2
|
550±50
|
1:1/10:1
|
20-30
|
2-3
|
25
|
SP-810
|
translucent
|
10
|
4000±1000
|
30±10
|
12±2
|
550±50
|
1:1/10:1
|
20-30
|
2-3
|
25
|
SP-815
|
translucent
|
15
|
4000±1000
|
35±10
|
14±2
|
550±50
|
1:1/10:1
|
20-30
|
2-3
|
25
|
SP-820
|
translucent
|
20
|
5000±1000
|
40±10
|
20±2
|
500±50
|
1:1/10:1
|
20-30
|
2-3
|
25
|
SP-825
|
translucent
|
25
|
6000±1000
|
45±10
|
22±2
|
500±50
|
1:1/10:1
|
20-30
|
2-3
|
25
|
SP-830
|
translucent
|
30
|
7000±1000
|
50±10
|
24±2
|
450±50
|
1:1/10:1
|
20-30
|
2-3
|
25
|