General characteristics
CSA BINDER is a hydraulic binder based on calcium sulphoaluminate, rather than calcium
aluminates which are the basis of CALCIUM ALUMINATE CEMENT or calcium silicates which
are the basis of PORTLAND CEMENT. The difference gives HCSA BINDER properties
particularly suited to formulators of products such as self-leveling or self-smoothing compounds,
rapid hardening screeds, tile adhesives, non-shrink grouts, rapid setting and special mortars.
CSA BINDER is used in formulated products either as a hydraulic binder by itself or with the
addition of calcium sulphates, or in combination with PORTLAND cement. The setting time is
quicker than that of PORTLAND cement, and it also has a rapid strength development. HCSA
BINDER does not release free lime during hydration thus eliminates the major cause of
efflorescence.
HCSA BINDER is manufactured under a strict quality assurance systems GB/T 19001-2000 (i.e.
ISO9001:2000) and GB/T 24001-1996 (i.e. ISO 14001:1996)) which accommodates the technical
requirements of building chemistry formulators.
The properties of HCSA BINDER conform to the standards of the manufacturer and to the
Chinese relevant standards.
Chemical Analysis
The chemical analysis of HCSA BINDER has been determined according to the following:
GB/T 176-1996 Methods of chemical analysis for cement
Main constituents (%)
|
|
SiO2
|
Al2O3
|
Fe2O3
|
CaO
|
MgO
|
TiO2
|
SO3
|
|
Usual range
|
4.5~6.5
|
32~39
|
1.0~2.0
|
39~41
|
1.5~2.0
|
1.0~1.5
|
9~11
|
|
Specification limit
|
＜7.0
|
＞35
|
＜2.5
|
39~42
|
＜2.5
|
＜1.8
|
9~12
|
Fineness
Specific Surface Area: according to standard GB/T 8074-1987
Usual range: 360~430 m2/kg
Specification limit: >360 m2/kg
Hydraulic Properties
The characteristics of HCSA BINDER have been tested in accordance with the Chinese standards.
- Setting time determined at 20 using Vicat needle, according to GB/T 1346-2001
- Mechanical strength at 20 , 95% relative humidity.
Mortar according to JC933-2003
|
Item
|
Type 1
|
Type 2
|
Type3
|
|
Bending Strength(Mpa)
|
1d
|
>8.0
|
>7.0
|
>6.0
|
|
3d
|
>10.0
|
>9.0
|
>8.0
|
|
7d
|
>11.0
|
>10.0
|
>9.0
|
|
Compressive strength
(Mpa)
|
1d
|
>60.0
|
>50.0
|
>50.0
|
|
3d
|
>85.0
|
>75.0
|
>65.0
|
|
7d
|
>95.0
|
>85.0
|
>75.0
|
|
Setting time
|
Initial
|
>25min
|
|
Final
|
<300min
|
Additional information
This information is given for reference only.
Mineral composition
C=CaO A=Al2O3 S=SiO2 F=Fe2O3 S= SO3
- Pricipal mineral phase: calcium sulphoaluminate C4 A3 S
- Secondary phases: C2S, C4AF
Reactivity with Portland cement
HCSA BINDER may be used in combination with other mineral products, for example
PORTLAND cement, calcium sulphates and fillers, or with organics such as polymers in latex
form or in redispersible form.
Depending on the type of mixes and technology employed, HCSA BINDER can be used to obtain
and control various properties.
The behaviour of PORTLAND cement is vary variable. In general, acceleration of set increases
progressly with the addition of HCSA BINDER. The amount of HCSA BINDER needed to obtain
a specific setting time varies considerably depending on the origin of the PORTLAND cement and
performance can be modified with the use of additives.
The strength development of HCSA BINDER/PORTLAND cement and/or Calcium Sulphates
depend on the nature of the PORTLAND cement and/or Calcium Sulphates used. In general these
mixes will develop mechanical strength at a very early stage (several hours). With some type of
PORTLAND cements and in formulated products containing additives which control the setting
and hydration, the long term properties is similar to those of the original PORTLAND cement,
however it is necessary to check the behaviour of each PORTLAND cement used.
The characteristics of PORTLAND cement to be considered are:
- C3A content
- Mineral admixture type and content
- Type of Calcium Sulphate used
Additives will also influence the properties of these mixes:
- Setting time
- Rheology
- Mechanical performance
These properties are applied to obtain a wide range of products:
- Fast setting cements
- Rapid hardening mortars
- Tile adhesives
- Self-leveling compounds
- Non-shrink grouts
- Water stopping mortars
- etc.
With a careful selection of the constituents (OPC, calcium sulphates, additives), it is possible to
create mixes with a range of different hydraulic properties:
- Adjustable setting time
- Rheology adapted to the application
- High early strength
- High long term strength
- Shrinkage compensation
Use of Additives
HCSA BINDER may be used in combination with chemical additives such as:
- polymers, either in latex form or redispersible powder form
- defoamers
- retarders
- accelerators
- plasticizers/superplasticizers
- rheology modifiers
- fibers
Package and Store
HCSA BINDER is normally supplied in one-tonne bag which include a moister resistant barrier.
However, in common with all hydraulic binders HCSA BINDER must be kept from moisture, and
can retain its properties for up to six months when properly stored.